Changzhou YIHE Composite Materials Co., Ltd
Quality control direction, service creation impact.
Add to Cart
It is a BOPET base product with an excellent matte finish that minimizes glare while preserving image as well as creating a luxury to the look of books, brochures, luxury packaging and other printed materials.
n Low level of static
n Excellent matte finish
n Excellent resistance to tear & elongation
| NO. | Properties | Unit | Value | Test Method | |
| 1 | Standard Thickness | mic | 12 | ||
| 2 | Film Thickness Tolerance | % | ≤ | 5 | ASTM-D374 |
| 3 | Tensile Strength MD | MPa | ≥ | 200 | ASTM-D882 |
| Tensile Strength TD | ≥ | 200 | |||
| 4 | Elongation at Break MD | % | ≥ | 100 | |
| Elongation at Break TD | ≥ | 100 | |||
| 5 | Heat Shrinkage(150℃/30min) MD | % | ≤ | 1.5 | ASTM-D1204 |
| Heat Shrinkage(150℃/30min) TD | ≤ | 0.5 | |||
| 6 | Wetting Tension | mN/m | ≥ | 52 | ASTM-2578 |
| 7 | WVTR | g/m2.24h | ≤ | 3.5 | ASTM-F1249 |
| 8 | OTR | cm3/(m2.24h.0.1MPa) | ≤ | 15 | ASTM-F1927 |
| 9 | Strong adhesive strength | % | ≤ | 20 | --- |
| 10 | Aluminum-plate thickness | OD | ≥ | 2.0 | --- |
| 11 | Aluminum-plate equality | % | ± | 15 | --- |
Laminating equipment: thermal laminating machine
Temperature: 95-120℃
Pressure: 8-18MPa
Speed:1-70m/min
Adjust the processing parameter according to the production job requirement.
n Keep upright in a clean, dry and ventilated warehouse; avoid storage in direct sunlight or near sources of heat less than 2m.
n In order to avoid damage to the film surface or end surface, avoid collision during product transportation, loading and unloading process.
n When used the thermal laminating film in winter, should put the film and laminating substrate in the operating room, balance the temperature higher than 18℃and then processed.
12 months.